Acid Sheet - HRP

Euro Quality : DD11 - DD11(Cu) - DD12 - DD13 - DD14

Erdemir Quality : 6222 – 6282 – 3222 – 3922 – 4222 - 7222

Width : 600 - 1550 mm

Wall Thickness : 1.5 - 5.00 mm

Acid Sheet - HRP

Acid Sheet - What is HRP?

Hot RolledScale (oxide) formed on the roll surfaces is cleaned by passing through Hydrochloric acid or Sulfuric acid baths and then again.oxidationIt is lubricated with protective oil to prevent

The product, which is called Acid Cleaned Sheet, is delivered to the user as a roll or as sliced ​​and cut paint according to the demand.

(RP-RPD- RPKK- HRP - HRPKK-LP-LPKK-TRP-TRPD-TRPKK)

HRP hot rolled, surface cleaned with acid, the edges are trimmedsheet cut from rollHRPKK Is it hot rolledş, sheet metal cut from a roll with the surface cleaned with acid and the edges of which are not trimmed 110

THRP Hot rolled,tempered, acid-cleaned sheet cut from coils with trimmed edges

THRPK Hot rolled,tempered, acid-cleaned sheet cut from coil with uncut edges

HRP Sheet Properties

HRP sacThe properties of this material are the basis of the fact that its products are becoming more and more common.HRP sheetsFirst of all, it has a high strength value. As they have undergone both hot and cold rolling procedureHRPThe resistances of the sheets are greatly increased. With thisHRP sheetscorrosion resistance is also higher than normal iron. Even in areas where the risk of corrosion is high, it is possible to use this material for many years without any problems.HRP sheetsIt also stands out with its resource retention levels. Able to bond strongly with other metalsHRP sheetsapplied resources can remain intact for a long time.

HR → HRP

Pickling Line

Material thickness

1.50 – 5.00 mm

Width

600 – 1550 mm

Coil Inner Diameter

610 mm

Maximum Roll Weight

30 ton

Quality

CONTINUOUS HOT ROLLED LOW CARBON STEEL FLAT PRODUCTS FOR COLD FORMING

No

(No)

Steel quality

(Steel Ouality)

Steel Its number

(Steel Number)

Product form (Form of Product)

Chemical Composition

(Chemica/ Compostion) ( % ) Max

Flowing Stress (Yield Strength)

(Nlmm2)

Flowing Stress (Yield Strength)

(Nlmm2)

Rupture Stress (Tensile Strength)

(Nlmm2)

Elongation amount (AND/ongation) (

¾)Min

Elongation amount (AND/ongation) (

¾)Min

Elongation amount

(Elongation) ( % ) Min

C

s;

Mn

p

s

1,00<e<2,00

mm

2,00<e<11,00

mm

RmMax.

1,00<e<1,50m

m

1,50<e<2,00m

m

2.00<3,00mm

one

DD11

1.0332

HAP*

0.12

-

0.60

0.045

0.045

170-360

170-340

440

22

23

28

2

DD12

1.0398

HAP*

0.10

-

0.45

0.035

0.035

170-340

170-320

420

24

25

30

3

0013

1.0335

HAP*

0.08

-

0.40

0.030

0.030

170-330

170-310

400

27

28

33

4

DD14

1.0398

HAP*

0.08

-

0.35

0.025

0.025

170-310

170-290

380

30

31

36

(*)Tot rolled pickled material

HOT ROLLED, HIGH STRENGTH STEEL FLAT PRODUCTS FOR COLD FORMING

No

(No)

Steel quality

(Steeı Ouality)

Steel Its number

(Steel Number)

Product form (Form of Product)

Chemical Composition

(Chemical Compostion) ( % ) Max

Flowing Stress (Yield Strength)

(Nlmm2)

(Min)

Rupture Stress (Tensile Strength)

(Nlmm2)

Elongation amount (Elongation) (

%,)Min

Elongation amount (Elongation) (

¾)Min

C

s;

Mn

p

s

Al(min)

one

S315MC

1.0972

HAP *

0.12

0.50

1.30

0.025

0.020

0.015

315

390-510

20

24

2

S355MC

1.0976

HAP *

0.12

0.50

1:50

0.025

0.020

0.015

355

430-550

19

23

3

S420MC

1.0980

HAP *

0.12

0.50

1.60

0.025

0.015

0.015

420

480-620

16

19

4

S550MC

1.0986

HAP *

0.12

0.50

1.80

0.025

0.015

0.015

550

600-760

12

14

(*)Tot rolled pickled material

HOT ROLLED CONSTRUCTION STEELS Hot-rolled products for structural steels (HRP-TS EN 10025-2)

No (No.)

Steel Quality(Steel Quality)

Steel Number(Steel Number)

Product Form(Form of Product)

Chemical Composition(Chemical Compostion) (%) Max

Yield Stress(Yield Strength) (N/mm2 ) (Min)

Shear Stress(Tensile Strength) (N/mm2 )

Elongation Amount (Elongation) ( %) Min

Elongation Amount (Elongation) ( %) Min

Elongation Amount (Elongation) (%)Min

Elongation Amount (Elongation) ( %) Min

Elongation Amount (Elongation) ( %) Min

C

Mn

P

s

N

With

Rm Max.

and<1,00mm

1,00<e<1,50m m

1,50<e<2,00mm

2,00<e<2,50m m

2,50<e<3,00 mm

one

S235JR

1.0037

HRP*

0.20

1.40

0.04

0.040

0.012

0.550

235

360-510

17

18

19

20

21

2

S275JR

1.0044

HRP*

0.22

1:50

0.04

0.040

0.012

0.550

275

430-580

15

16

17

18

19

3

S355JR

1.0045

HRP*

0.24

1.60

0.04

0.040

0.012

0.550

355

510-680

14

15

16

17

18

Low Carbon Hot Rolled Steels Suitable for Cold Forming Chemical Composition (%)

Standard Equivalent

ERDEMIR

Quality No.

Deoxidationmethod

C max.

Mn max.

P max.

S max.

Of mine

Standard

Quality

IN 10111

DD11

3222

-

0.12

0.60

0.045

0.045

-

IN 10111

DD11

4222

-

0.12

0.60

0.045

0.045

-

IN 10111

DD11

6222

-

0.11

0.5

0.035

0.035

-

IN 10111

DD11

6282(one)

-

0.12

0.60

0.045

0.045

-

IN 10111

DD12

6223(3)

fully stagnant steel

0.09

0.4

0.03

0.030

-

IN 10111

DD13

6224(2)3)

fully stagnant steel

0.07

0.35

0.025

0.025

-

IN 10111

DD11

7222

-

0.12

0.60

0.045

0.045

-

IN 10111

DD14

7224(3)

fully stagnant steel

0.08

0.35

0.025

0.025

0.01

Mechanical Properties

Standard Equivalent

ERDEMIR

Quality No.

RandN/mm2 ( kg/mm2 )

Rm(one)

N/mm2 ( kg/mm2 )

A (%)

Guarantee13) Time

A80

A5

Standard

Quality

1.5 < d < 2

2 < d < 11

max.

1.5 < d < 2 min.

2 < d < 3 min.

3 < d < 11 min.

IN 10111

DD11

(2)

3222

170 - 360 (17.3-36.7)

170 - 340 (17.3-34.7)

440

(44.9)

23

24

28

-

IN 10111

DD11

(2)

4222

170 - 360 (17.3-36.7)

170 - 340 (17.3-34.7)

440

(44.9)

23

24

28

-

IN 10111

DD11

(2)

6222

170 - 360 (17.3-36.7)

170 - 340 (17.3-34.7)

440

(44.9)

23

24

28

-

IN 10111

DD11

(2)

6282

170 - 360 (17.3-36.7)

170 - 340 (17.3-34.7)

440

(44.9)

23

24

28

-

IN 10111

DD11

(2)

7222

170 - 360 (17.3-36.7)

170 - 340 (17.3-34.7)

440

(44.9)

23

24

28

-

IN 10111

DD12

6223

170 - 340 (17.3-34.7)

170 - 320 (17.3-32.6)

420

(42.8)

25

26

30

6 is

IN 10111

DD13

6224

170 - 330 (17.3-33.7)

170 - 310 (17.3-31.6)

400

(40.8)

28

29

33

6 is

IN 10111

DD14

7224

170 - 310 (17.3-31.6)

170 - 290 (17.3-29.6)

380

(38.8)

31

32

36

6 is

Usage Areas

These materials producedsurface smoothness, thickness, width and physical properties are produced according to expectations. In general, the area where they are applied is suitable for cold forming. Accordingly, kitchen utensils, ventilation, durable household appliances, automotive sector and radiator. It can be used in applications that users want.

In the white goods sector, in the automotive sector, superiormalleablelIIt is used in areas suitable for aging resistance and outstanding extra deep drawing processes.

Deep draw featureIt is used during the manufacture of steels and kitchen utensils that are suitable for enamel coating. (For example, items such as pots, oven grates, etc.) It may not always be appropriate to use due to scale on the surface of hot rolled sheets. Hot rolled degreased and pickled grades are generally used for deep drawing, bending and drawing processes.

These products do not have sensitive surface quality expectations. Howeverrijitlik, strength andyour plasterabilityIt can be used in all applications where it is required. The surface of the machines in the manufacturing sector, as well as in the automotive side secondsSheets cleaned with acidis used. Cleaning the surface of the sheets with acid provides more economic benefits after machine manufacturing. For this reason, manufacturers generally prefer materials whose surface is cleaned with acid.

Suitable for cold forminghigh strength steels with high impact,can be shapedrnessand it can be preferred in all applications requiring fatigue resistance. LPG cylindersIt has been used successfully during production. These products, which are used successfully in the building sector, are preferred because they can be shaped in general.

Weight Chart

Thickness mm

Unit Weight (kg) Size (width x height)

1200x2400

1250 x 2500

1500 x 3000

1500 x 6000

1500x12000

2000x6000

2000 x 8000

2000x12000

2500 x 12000

3000 x 12000

6

136

147

212

424

848

565

754

1130

1413

1696

8

181

196

283

565

1130

754

1005

1507

1884

2261

10

226

245

353

707

1413

942

1256

1884

2355

2826

12

271

294

424

848

1696

1130

1507

2261

2826

3391

14

317

343

495

989

1978

1319

1758

2638

3297

3956

15

339

368

530

1060

2120

1413

1884

2826

3533

4239

16

362

393

565

1130

2261

1507

2010

3014

3768

4522

18

407

442

636

1272

2543

1696

2261

3391

4239

5087

20

452

491

707

1413

2826

1884

2512

3768

4710

5652

22

497

540

777

1554

3109

2072

2763

4145

5181

6217

25

565

613

883

1766

3533

2355

3140

4710

5888

7065

30

678

736

1060

2120

4239

2826

3768

5652

7065

8478

32

723

785

1130

2261

4522

3014

4019

6029

7536

9043

35

791

859

1236

2473

4946

3297

4396

6594

8243

9891

40

904

981

1413

2826

5652

3768

5024

7536

9420

11304

45

1017

1104

1590

3179

6359

4239

5652

8478

10598

12717

50

1130

1227

1766

3533

7065

4710

6280

9420

11775

14130

55

1243

1349

1943

3886

7772

5181

6908

10362

12953

 

60

1356

1472

2120

4239

8478

5652

7536

11304

14130

 

70

1583

1717

2473

4946

9891

6594

8792

13188

 

 

80

1809

1963

2826

5652

11304

7536

10048

 

 

 

90

2035

2208

3179

6359

12717

8478

11304

 

 

 

one hundred

2261

2453

3533

7065

14130

9420

12560

 

 

 

110

2487

2698

3886

7772

 

10362

 

 

 

 

120

2713

2944

4239

8478

 

11304

 

 

 

 

130

2939

3189

4592

9185

 

12246

 

 

 

 

150

3391

3680

5299

10598

 

14130

 

 

 

 

200

4522

4906

7065

14130